System Three - Clear Coat
- SKU:
- S3-CC-PARENT
Description
Clear Coat is an extremely low viscosity, water white, "penetrating" epoxy system. Clear Coat cures to a brilliantly clear, very tough finish without the usual "amine blush" associated with some epoxy resin films. Clear Coat contains no volatile solvents.
Clear Coat is ideal for clear coating wood, and the wetting out of fiberglass cloth for bright finished boats. Use as a build coat for clear linear polyurethane or varnish coatings and as a penetrating first coat for blister repair on fiberglass boats. Use also for those applications that require a long pot life and low viscosity. Use Clear Coat as the sole epoxy system to make wood strip canoes and kayaks. Protect Clear Coat from moisture during cure to avoid water spotting.
- Features a convenient 2:1 mixing ratio.
- A clear, almost water-white, solvent-free epoxy system.
- Cures to a clear, glossy, blush-free surface.
Physical Properties
| Mix Ratio by Volume | 100:50 |
| Mix Ratio by Weight | 100:43 |
| Total Solids | 100% |
| Mixed Viscosity | 380 cps |
| Minimum Application Temperature | 50°F (10°C) |
| Tensile Strength, psi | 7,800 |
| Tensile Elongation at Break | 8% |
| Flexural Strength, psi | 12,000 |
| Flexural Modulus, psi | 375,000 |
| Compressive Strength, psi | Yield 13,000 |
| Failure | 26,000 |
| Coverage | See Product Usage Estimations Chart |
| Gel Time @ 77°F (25°C) | 60 Minutes (100g mixture) |
| Tack FreeTime Thin Film @ 77°F (25°C) | 24 Hours |
| Full Cure @ 77°F (25°C) | 72 Hours |
Related Products
Quick Cure 5 by System Three
Polyester Three Strand Rope
Polypro Three Strand Rope
Stainless Steel Coat Hook
Seadog Brass Double Coat Hook
An inexpensive, durable oarlock system
Small Boat Head System